13549213581 肖生

 

MALECCA K-300

丙烯腈丁二烯苯乙烯

DENKA

 

Technical Data

 

产品说明

 

MALECCA is a high heat resistant ABS resin which is based on styrene-N-phenylmaleimide copolymer. MALECCA was developed by Denka using their advanced polymerization technologies. This high heat ABS is much more highly improved in the areas of heat stability, processing characteristics and impact strength over traditional alpha-methylstyrene-based resins and is very easy to use.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet (English)

UL 黄卡 2 •  E49895-241476

搜索 UL 黄卡 •  DENKA

•  MALECCA

供货地区 • 北美洲 • 欧洲 • 亚太地区

加工方法 • 注射成型

物理性能 额定值单位制 测试方法

比重

-- 1.06g/cm³ ASTM D792

23°C 1.08g/cm³ ISO 1183

熔流率（熔体流动速率） (220°C/10.0 kg) 4.0g/10 min ISO 1133

收缩率 (2.00 mm) 0.50 到 0.80% 内部方法

机械性能 额定值单位制 测试方法

拉伸模量

-- 4 41.0MPa ASTM D638

-- 2450MPa ISO 527-2/1

拉伸应力 ISO 527-2/50

屈服 48.0MPa

断裂 40.0MPa

标称拉伸断裂应变 21% ISO 527-2/50

弯曲模量

-- 5 2250MPa ASTM D790

-- 6 2450MPa ISO 178

弯曲强度

-- 5 75.0MPa ASTM D790

-- 6 79.0MPa ISO 178

冲击性能 额定值单位制 测试方法

简支梁缺口冲击强度 16kJ/m² ISO 179

悬壁梁缺口冲击强度 180J/m ASTM D256

硬度 额定值单位制 测试方法

洛氏硬度

R 级 114 ASTM D785

R 计秤 116 ISO 2039-2

热性能 额定值单位制 测试方法

载荷下热变形温度

1.8 MPa, 未退火 7 110°C ASTM D648

1.8 MPa, 未退火 100°C ISO 75-2/Af

维卡软化温度 120°C ISO 306/B 8

ASTM D1525

可燃性 额定值单位制 测试方法

UL 阻燃等级 HB UL 94

 

 

MALECCA K-300

丙烯腈丁二烯苯乙烯

DENKA

注射 额定值单位制

干燥温度 90.0 到 100°C

干燥时间 3.0 到 4.0hr

料筒后部温度 210 到 230°C

料筒中部温度 220 到 250°C

料筒前部温度 230 到 260°C

模具温度 50.0 到 80.0°C

背压 0.490 到 0.981MPa

螺杆转速 50 到 80rpm

 

 

 

 

 

 

 